ISO-epoxy 'M' sheet consists of muscovite mica paper impregnated with a selected epoxy resin.
ISO-epoxy sheets are sanded with a precise tolerance and are used for all sizes of commutators.

Propreties for ISO-Epoxy M (standard: IEC 371-2):
- Composition: mica 90% and resin epoxy 10%
- Dielectric strength: 20 KV/mm
- Density: 2,2 to 2,6 kg/dm³
- Flexural strength: 300 Mpa
- Compressibility: 2 to 2,5%
- Resistance to exudation and displacement: 300 °C
- Thickness: 0,4 to 2 mm
- Thickness tolerance: ±0,02 mm


Dimensions standard:
960 x 600 mm

 

The ISO-Flex products are designed for the metal smelting industry to separate the refractory linings from coils in induction furnaces. The barrier created by the ISO-Flex products provides protection from carbon gases and protects the inductor coils from expansion and contraction forces caused by thermal gradients.

The ISO-Flex products also provide electrical insulation between the coil and the molten metal, optimizing the heat flow and preventing leakage and costly damage to the coil. Several grades of flexible ISO-Flex products are available. Each of them offers specific feature depending on their composition.

Available in rolls with standard length 25 or 50 meters and thickness 0,20 to 0,50 mm. This product is constituted of impregnated Phlogopite Mica paper reinforced with glass cloth inside. It allows an excellent heat transfer and replaces advantageously the usual products used for sintering process.

Dimensions:
- Thickness: 0.20 to 0.50 mm
- Width: 1000 mm
- Roll length: 25 or 50 m (core diameter: 150 mm)


Composition:
- Mica type Phlogopite
- Reinforced with glass cloth inside
- Mica content: min 90%
- Silicone binder content: max 10%
- Dielectric strength (23°C): 10 KV/mm

Available in sheets with maximum length 2400mm, width 1000mm and thickness from 0.50 up to 5mm (or more). This products is constituted of impregnated Phlogopite Mica paper and its good flexibility allows an easy handling and application.

Dimensions:
- Thickness: 0.50 to 5.00 mm
- Width: 1000 mm
- Length: max 2400 mm

Composition:
- Mica type Phlogopite
- Mica content: min 90%
- Silicone binder content: max 10%
- Dielectric strength (23°C): 10 KV/mm

The ISO-Combi material is a AES fiber paper laminated item. It offers the lowest thermal conductivity.
The selected AES fiber paper is 100% free of toxicity and does not require any specific protection for handling. AES paper should be placed against the coil.
Mica is reinforced with glass cloth for a better tensile strength during handling and application.

Dimensions:
- Thickness: 2.3 mm and 2.5 mm depending on the mica content (other dimensions available on special request)
- Width: 1000 mm or 500 mm or 250 mm
- Roll length: 12.5 or 25 m rewound on a hard paper core (ID 150 mm) (other dimensions also available)

Composition:
ISO-Combi 350-2
- Mica type Phlogopite
- Mica content: 350 g/m²
- Silicone binder content: 20 g/m²
- AES fiber paper content: 450 g/m²
- Dielectric strength (23°C): > 4 kV
- Total Thickness: 2,3 mm

ISO-combi 520-2
- Mica type Phlogopite
- Mica content: 520 g/m²
- Silicone binder content: 30 g/m²
- AES fiber paper content: 450 g/m²
- Dielectric strength (23°C): > 6 kV
- Total Thickness: 2,5 mm

Non-woven AES bio soluble fibers paper, ISO-Ceram offers exceptional insulation performance and flexibility with excellent handling strength.
Typical applications of ISO-Ceram are aluminium transfer system back up insulation, induction ovens insulation, automotive heat shields and silencer insulation. ISO-Ceram is also a good high temperature gasket.
Iso-Ceram is available in different thicknesses from 1,00 to 8,00 mm. Standard lengths are 30 and 60 m and 1 m wide. Other dimensions on request.

Composition:
- SiO2: 64%
- CaO: 30%
- MgO: 4,5%
- Other: 1,5%

Mechanical properties
- Melting point min: 1330°C
- Thermal Conductivity:
   400°C: 0,06 W/m°K
   600°C: 0,09 W/m°K
   800°C: 0,14 W/m°K
- Density: min 200 kg/m³ - max 300 kg/m³
- Loss in ignition: 12 %
- Tensile strength (2mm thick paper): 7 N/cm

ISO-Therm is a Mica laminate used in electro and thermo-electrical applications.
Because of its resistance to heat and its excellent electrical insulation, ISO- Therm is one of the best materials to replace Asbestos.
Composed of Muscovite ('M') or Phlogopite ('P') Mica and silicon resin pressed under high pressure and temperature, ISO-Therm is recommended when the continuous service conditions can reach 500°C and beyond.

Mechanical Properties for ISO-Therm M:
- Density: 2.1 Kg/dm³ (standard: IEC-371-2)
- Tensile strength: 150 Mpa (standard: ISO 527)
- Heat resistance: 550°c
- Loss of weight: < 1 %
- Thermal conductivity (perpendicular): 0.3 W/m°K
- Water absorption (24h at 25°C): < 1 %
- Dielectric strength: 25 KV/mm (standard: IEC 243)

Dimensions:
- Thickness: 0.2 to 75 mm
- Sheet size: 1200x1000 mm or 2000x1000 mm or 2420x1020mm

Mechanical Properties for ISO-Therm P:
- Density: 2.1 Kg/dm³ (standard: IEC-371-2)
- Tensile strength: 110 Mpa (standard: ISO 527)
- Heat resistance: 700°c
- Loss of weight: < 1 %
- Thermal conductivity (perpendicular): 0.3 W/m°K
- Water absorption (24h at 25°C): < 1 %
- Dielectric strength: 25 KV/mm (standard: IEC 243)

Dimensions:
- Thickness: 0.2 to 75 mm
- Sheet size: 1200x1000 mm or 2000x1000 mm or 2420x1020mm

ISO-Tubes are used when the assembly of complicated mica pieces required metallic parts.
Designed on customer request, ISO-Tubes surround and insulate the metallic screws and bolts.

Dimensions:
- Length: max 1000 mm (range +/- 1mm)
- Outside diameter: max 460 mm (range +/-0,5 mm)
- Inside diameter: min 6 mm (range +/-0,3 mm)
- Thickness: min 0,25 mm - max 30 mm

Composition:
- Mica: min 90 % (standard IEC 371-2)
- Silicon binder: max 10% (standard IEC 371-2)
- Dielectrique strength: min 20 KV/mm (standard IEC 371-2 at 20°C)
- Density: min 1.2 kg/dm³
- Heat resistance: Muscovite max 500°C - Phlogopite max 700°C

ISO-Cable Tape consists of Phlopgopite mica paper bonded to an electrical grade glass cloth. Both materials have been impregnated with a specific high temperature resistant silicone resin.
ISO-Cable Tape offers excellent flame-resisting characteristics. When exposed to a flame, the silicone binder turns into inorganic silicone dioxide which offers a high electrical insulation at high temperature.
ISO-Cable Tape is free of halogens and toxic gases. Due to the high flexibility, these tapes can be easily applied with high speed taping machines in one or two layers depending on the requirements of the cable.

Dimensions:
- Thickness: 0,1 mm (min 0,08 mm - max 0,12 mm) or 0,12 (min 0,105mm - max 0,135 mm) (standard IEC 371-2:20°C and HR 50%)
- Width: from 6 mm to 1000 mm

Composition:
- Mica content: min 73 g/m² - max 87 g/m²
- Silicone binder: min 11 g/m² - max 17 g/m² (standard IEC 371-2:20°C and HR 50 %)
- Glass cloth: average 34 g/m²

Properties:
- Flexural strength: min 50 N/m - 20 KV/mm (standard IEC 371-2:20°C and HR 50 %)
- Weigth loss (2 hours at 200°C): < 0,5 % (standard IEC 371-2)
- Water absorption (24 hours at 20°C): < 0,5 % (standard IEC 371-2)
- Dielectric strength: 1.1KV/layer (standard IEC 371-2:20°C)
- Tensile strength: 100 N/cm (standard ISO 527:20°C)